IMPROVING AIRCRAFT PARTS DUE TO USING NANO-COMPOSITE AND MICRO-COMPOSITE MATERIAL

Abstract

In this paper it is investigated how to make composite carbon nanofiber/ epoxy resin and carbon micro-fiber / epoxy resin. Also, these materials' features are compared and it is shown how effective and benefitial are the received products containing carbon nano- and micro-fibers.In this study, epoxy composites were prepared in order to improve their mechanical and electrical properties. Ergo, carbon nanofibers and carbon microfibers were used as fillers. On the one hand, purchased microfibers were incorporatedinto the epoxy resin to produce epoxy/carbon microfiber composites via mechanical mixing at 1800 rpm in different concentrations (0.0125, 0.0225, 0.05, and 0.1).On the other hand, carbon nanofibers were prepared via electrospining method at room temperature, then epoxy/carbon nanofiber nanocomposites were prepared at mixing temperature of 60 °C at 1200 rpm at different concentrations (0.0125, 0.05, and 0.1).Morphology of samples was investigated via Field Emission Scanning Electron Microscopy (FESEM). Mechanical properties of samples were investigated via tensile and bending tests. Tensile test results revealed that incorporation of 0.0125 wt% carbon naofibers increased the epoxy resins modulus about 200%. Bending strength of sample containing 0.1wt% carbon microfibers had the most increment (from 20 to 100 MPa).

About the Author

H. M. Boer
Tarbiat Modares University
Islamic Republic of Iran

Engineer of the manufacturing airplanes and helicopters,

Tehran



References

1. Fan F.R., Lin L., Zhu G., Wu W., Zhang R., Wang Z.L. Transparent triboelectric nanogenerators and self-powered pressure sensors based on micropatterned plastic films. Nano Letters, vol. 12, no. 6, pp. 3109–3114, 2012.

2. Park K.-I., Xu S., Liu Y. et al. Piezoelectric BaTiO3 thin film nanogenerator on plastic substrates. Nano Letters, vol. 10, no. 12, pp. 4939–4943, 2010.

3. Kumar B., Kim S.-W. Recent advances in power generation through piezoelectric nanogenerators. Journal of Materials Chemistry, vol. 21, no. 47, pp. 18946–18958, 2011.

4. Chang J., Dommer M., Chang C., Lin L. Piezoelectric nanofibers for energy scavenging applications. Nano Energy, vol. 1, no. 3, pp. 356–371, 2012.

5. Khnayzer R.S., Thompson L.B., Zamkov M. et al. Photocatalytic hydrogen production at titania-supported Pt nanoclusters that are derived from surface-anchored molecular precursors. The Journal of Physical Chemistry C, vol. 116, no. 1, pp. 1429–1438, 2012.

6. Chaudhari S., Sharma Y., Archana P.S. et al. Electrospun polyaniline nanofibers web electrodes for supercapacitors. Journal of Applied Polymer Science, vol. 129. no. 4, pp. 1660–1668, 2013.

7. Kurban Z. Electrospun nanostructured composite fibres for hydrogen storage applications [Doctoral thesis]. Department of Physics and Astronomy University College. London. UK. 2011.

8. Jongh P.E., Adelhelm P. Nanosizing and nanoconfinement: new strategies towards meeting hydrogen storage goals. ChemSusChem, vol. 3, no. 12, pp. 1332–1348, 2010.

9. Fichtner M. Nanoconfinement effects in energy storage materials. Physical Chemistry Chemical Physics, vol. 13, no. 48, pp. 21186–21195, 2011.

10. Nielsen T.K., Besenbacher F., Jensen T.R. Nanoconfined hydrides for energy storage. Nanoscale, vol. 3, pp. 2086–2098, 2011.

11. Xia G., Li D., Chen X. et al. Carbon-coated Li3N nanofibers for advanced hydrogen storage. Advanced Materials, vol. 25, no. 43, pp. 6238–6244, 2013.

12. Alipour J., Shoushtari A.M., Kaflou A. Electrospun PMMA/AB nanofiber composites for hydrogen storage applications. e-Polymers, vol. 14, no. 5, pp. 305–311, 2014.


Review

For citations:


Boer H.M. IMPROVING AIRCRAFT PARTS DUE TO USING NANO-COMPOSITE AND MICRO-COMPOSITE MATERIAL. Civil Aviation High Technologies. 2017;20(3):59-64. (In Russ.)

Views: 584


Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 License.


ISSN 2079-0619 (Print)
ISSN 2542-0119 (Online)