Influence of impurities contained in fuel and air on sulfide corrosion of turbine blades of the gas turbine engine

In the process of improving gas turbine engines (GTE), increasing the resource and efficiency, there is a constant increase in temperature and pressure of the working fluid. Turbine elements are subjected to high thermomechanical loads and continuous exposure from the aggressive environment. These impacts are especially significant for the working blades of the first stages of the turbine, located in the area of the highest temperatures. One of the most serious types of damage in this case is the corrosive effect on the working blade from the combustion gases entering the flow part of the turbine. The TS-1 fuel used on an aircraft contains sulfur compounds in its composition – elemental sulfur and mercaptans, which in the combustion process, together with sodium and potassium in the air, leads to an aggressive effect on the material of the turbine blade. To ensure the long-term operation of the turbine blades of the turbine at the gas temperature at the turbine inlet up to 800...850 ℃, the content of these products in both fuel and air is limited according to the regulatory and technical documentation. However, it is not yet possible to exclude them completely. The presence of sulfur compounds on the turbine blades of the GTE causes sulfide corrosion. Therefore, the article considers the influence of impurities in fuel and air on the process of sulfide corrosion of the turbine blades material of the turbine. The mechanism of sulfur dissolution in metal oxides or protective coating is presented, as well as the diffusion of sulfur oxide from the coating surface into its depth. The reason for the influence of sodium chloride contained in the air on the corrosion of nickel alloy or the protective coating applied on it has been established. The influence of vanadium in the fuel on the corrosion rate is given. In order to increase the efficiency of the turbine blades when exposed to such an aggressive environment, it is proposed to use a new coating formed from an aqueous suspension and allowing the introduction of chromium into the coating, which provides a higher durability of such a coating in comparison with serial aluminide coatings. The introduction of chromium is ensured by an exothermic reaction occurring during the formation of the coating during heat treatment.

1. Abraimov, N.V. & Eliseev, Yu.S. (2001). [Chemical and thermal treatment of heat-resistant steels and alloys]. Moscow: Intermet Inzhiniring, 622 p. (in Russian)

2. Muboyadzhyan, S.A., Lesnikov, V.P. & Kuznetsov, V.P. (2008). [Complex protective coatings for turbine blades of aircraft gas turbine engines]. Yekaterinburg: Kvist, 208 p. (in Russian)

3. Nikitin, V.I. (1987). [Corrosion and protection of gas turbine blades]. Leningrad: Mashinostroyeniye, 272 p. (in Russian)

4. Gishvarov, A.S. (2014). [Damage rate of power plants materials in a corrosive environment]. Moscow: Mashinostroyeniye, 297 p. (in Russian)

5. Kolomytsev, P.T. (1991). [Protective coatings for nickel alloys]. Moscow: Metallurgiya, 154 p. (in Russian)

6. Davydov, M.N., Gishvarov, A.S. & Rahimov, A.H. (2016). Modeling of durability of turbine blades in the corrosive environment. Vestnik UGATU, vol. 20, no. 1 (71), pp. 71–80. (in Russian)

7. Kachanov, E.B. & Tamarin, Yu.A. (2005). [Coatings to protect turbine blades fromsulfide corrosion]. Tekhnologiya legkikh splavov, no. 1–4, pp. 171–180. (in Russian)

8. Karpinos, B.S., Barilo, V.G. & Samuleev, V.V. (2004). [Destruction of elements of the hot path of aviation gas turbines]. Vestnik dvigatelestroyeniya, no. 1, pp. 4–10. (in Russian)

9. Yushchenko, K.A. & Savchenko, V.S. (2005). [High-temperature gas corrosion of nickel alloy turbine blades during operation]. Automatic welding, no. 5, pp. 25–34. (in Russian)

10. Mahobia, G.S., Paulose, N., Mannan, S.L., Sudhakar, R.G., Chattopadhyay, K., Santhi Srinivas, N.C. & Singh, V. (2014). Effect of hot corrosion on low cycle fatigue behavior of superalloy IN718. International Journal of Fatigue, vol. 59, pp. 272–281. DOI: 10.1016/j.ijfatigue.2013.08.009

11. Yang, X., Li, S. & Qi, H. (2015). Effect of high-temperature hot corrosion on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy. International Journal of Fatigue, vol. 70, pp. 106–113. DOI: 10.1016/j.ijfatigue.2014.08.011

12. Matrelov, V.N. & Piskunov, V.A. (1986). [Jet engines and fuel]. Moscow: Mashinostroyeniye, 293 p. (in Russian)

13. Khimich, V.L. & Kuznetsov, Yu.P. (2015). About the mechanism of salt scaling in the flow section of a gas turbine engine operating in the marine environment. Sovremennyye problemy nauki i obrazovaniya, no. 1-1, pp. 99. (in Russian)

14. Gryadunov, K.I. (2021). [Chemmotology of aviation fuels and lubricants: lecture texts]. Moscow: ID Akademii Zhukovskogo, 184 p. (in Russian)

15. Bokshtein, B.S. (1978). [Diffusion in metals]. Moscow: Metallurgiya, 248 p. (in Russian)

16. Wagner, C. (1933). Beitrag zur theorie des anlaufvorgangs. Zeitschrift für Physikalische Chemie, vol. 21B, no. 1, pp. 25–41. DOI: 10.1515/zpch-1933-2105

17. Chaug, R., Stewart, W. & Wagner, C. (1972). Diffusion of sulfur 35 NiO and CoO. Proceedings of the International Symposium on Reactivity of Solids. Bristol, 17–21 July. Chapman and Hall, Ltd., p. 231.

18. Gilder, X. & Merbiola, R. (1981). [Sulfide corrosion of alloys based on nickel and cobalt]. Zharoprochnyye splavy dlya gazovykh turbin: materialy mezhdunarodnoy konferentsii, in D. Kotsoradis, P. Felix, H. Fishmeister et al. (Eds.). Moscow: Metallurgiya, pp. 59–79. (in Russian)

19. Ivanov, E.G., Zorichev, A.V., Samoylenko, V.M. & Pashchenko, G.T. (2008). [New heat-resistant coating]. Defense Industry Achievements – Russian Scientific and Technical Progress, no. 3, pp. 22–24. (in Russian)

20. Ivanov, E.G., Samoylenko, V.M., Ravilov, R.G. & Petrova, M.A. (2015). Application of the aqueous coating suspension for the protection of gas turbine engine parts from corrosion. Nauchnyy Vestnik MGTU GA, no. 217, pp. 46–50. (in Russian)